EPUSELF 140/8 is a three-component mineral cast polymer based on an epoxy resin including a special filler combination consisting of raw materials.
Application
For casting large-volume machine parts ( pillars , machine stands and engine beds ) as well as substructures for assemblies strained by vibration e.g. engines, gear, turbines, centrifuges and test rigs.
For casting steel welding constructions to get a higher static and dynamic rigidity.
Properties
- Good rigidity
- Best vibration absorption
- Less sensitive to heat
- Adjustment to the coefficient of thermal expansion on steel
- Lowest creeping behaviour under load
List prices for purchase quantities of:
Quantity | Price per kg in € plus VAT |
0 - 500 kg | 5,30 |
501 kg - 1.000 kg | 5,10 |
1.001 kg - 3.000 kg | 4,90 |
Density | approx. 2,3 g/cm³ |
Compressive strength1 | > 130 MPa |
Flexural strength1 | > 30 MPa |
Modulus of elasticity | > 35,5 GPa (dynamic2) > 35,0 GPa (static1) |
Thermal expansion coefficient | approx. 17 * 10-6 K-1 at 20 °C |
Thermal conductivity | approx. 2,8 W/m K at 25 °C |
Specific heat capacity | approx. 0,8 J/g K at 25 °C |
Thermal diffusivity | approx. 1,7 mm 2/s at 25 °C |
Logarithmic decrement | 0,03 |
Wall thickness of cast | > 40 mm |
Maximum grain size | 8 mm |
Mixing ratio | A : B : C = 1,65 : 0,45 : 22,9 |
Processing time | approx 1 - 1,5 h at 23°C |
Processing temperature | 15 - 25°C |
Curing Time | approx. 24 h |
1 measured using: test frame Form + Test Seidner, Typ 502/3000/100SP
2 measured using: sound-resonance-analysis, RA100 Concrete, Lang Sensorik
Brochure Do-it-yourself mineral casting EPUSELF
The high-performance mineral casting system for do-it-yourself filling and casting of vibration-damping ...
Brochure
Download PDF (1 MB)English
Broschüre Mineralguss zum Selbermachen EPUSELF
Das leistungsfähige Mineralguss-System zum Selbstverfüllen und -vergießen von schwingungsdämpfenden Bauteilen ...
Brochure
Download PDF (1 MB)German